Chapter 15 Multiple Choice

(a).

As particle size increases, inter particle friction (a) decreases, (b) increases, or (c) remains the same?

(b) and (c)

For a given weight of metallic powders, the total surface area of the powders is increased by which of the following (two best answers): (a) larger particle size, (b) smaller particle size, (c) higher shape factor, and (d) smaller shape factor?

(b) and (c)

Impregnation refers to which of the following (two best answers): (a) filling the pores of the PM part with a molten metal, (b) putting polymers into the pores of a PM part, (c) soaking oil by capillary action into the pores of a PM part, and (d) something that should not happen in a factory?

(a)

In cold isostatic pressing, the mold is most typically made of which one of the following: (a) rubber, (b) sheetmetal, (c) textile, (d) thermosetting polymer, or (e) tool steel?

(a)

Repressing refers to a press working operation used to compress a sintered part in a closed die to achieve closer sizing and better surface finish: (a) true or (b) false?

(b). The given description neglects consideration of the screen wire thickness.

The particle size that can pass through a screen is obtained by taking the reciprocal of the mesh count of the screen: (a) true or (b) false?

(a), (b), (c)

Which of the following design features would be difficult or impossible to achieve by conventional pressing and sintering (three best answers): (a) outside rounded corners, (b) side holes, (c) threaded holes, (d) vertical stepped holes, and (e) vertical wall thickness of 1/8 inch (3 mm)?

(b).

Which of the following most closely typifies the sintering temperatures in PM? (a) 0.5Tm, (b) 0.8Tm, (c)Tm, where Tm = melting temperature of the metal?

(a), (b), and (e)

Which of the following processes combines pressing and sintering of the metal powders (three best answers): (a) hot isostatic pressing, (b) hot pressing, (c) metal injection molding, (d) pressing and sintering, and (e) spark sintering?

(a), (c), and (e)

Which of the following statements is correct in the context of metallic powders (three correct answers): (a) porosity + packing factor = 1.0, (b) packing factor = 1/porosity, (c) packing factor = 1.0 - porosity, (d) packing factor = - porosity, (e) packing factor = bulk density/true density?

(d)

hich of the following powder shapes would tend to have the lowest interparticle friction: (a) acicular, (b) cubic, (c) flakey, (d) spherical, and (e) rounded?